Revealing Superstructure Ordering in Co1+xMnSb Heusler Alloys and Its Effect on Structural, Magnetic, and Electronic Properties

We have performed a combined experimental and theoretical study of the Co1??xMnSb system to understand the progressive evolution of the crystal structure and physical properties as a function of Co content. We find that all the arc-melted polycrystalline samples show superstructure ordering similar to CoMnSb. In the CoMnSb superstructure with Fm-3m symmetry, one set of the 32 f sites is filled with Co atoms while the other set is vacant. With increasing Co content, although the vacant set of 32 f sites gets progressively filled with the Co atoms, some of the Co atoms segregate out of the main phase into the grain boundaries. The maximum Co that enters in the Co1??xMnSb phase is x = ???0.45. Thus, we find that the theoretically predicted Co2MnSb in L21 phase does not stabilize. All the samples are ferromagnetic above room temperature and the trend in the measured magnetic moments with increasing x, agrees reasonably well with the density-functional theory calculations done using the structural and compositional parameters obtained from the Rietveld refinement of the synchrotron x-ray diffraction patterns. However, the electronic structure indicates that in spite of the large magnetic moment, none of the alloys are half metallic. Finally, we find that a minor deviation from stoichiometry in CoMnSb, i.e., excess of Co and Sb as compared to Mn, is accommodated in the set of vacant 32 f sites of the superstructure. This explains the increase in the lattice parameter and the saturation magnetization, as compared to the calculated stoichiometric CoMnSb superstructure. Calculations also predict that this minor deviation from stoichiometry destroys the half metallicity in the CoMnSb superstructure.