Towards a Monolithically Integrated III–V Laser on Silicon: Optimization of Multi-Quantum Well Growth on InP on Si

High-quality InGaAsP/InP multi-quantum wells (MQWs) on the isolated areas of indium phosphide on silicon necessary for realizing a monolithically integrated silicon laser is achieved. Indium phosphide layer on silicon, the pre-requisite for the growth of quantum wells is achieved via nano-epitaxial lateral overgrowth (NELOG) technique from a defective seed indium phosphide layer on silicon. This technique makes use of epitaxial lateral overgrowth (ELOG) from closely spaced (1 mu m) e-beam lithography-patterned nano-sized openings (similar to 300 nm) by low-pressure hydride vapor phase epitaxy. A silicon dioxide mask with carefully designed opening patterns and thickness with respect to the opening width is used to block the defects propagating from the indium phosphide seed layer by the so-called necking effect. Growth conditions are optimized to obtain smooth surface morphology even after coalescence of laterally grown indium phosphide from adjacent openings. Surface morphology and optical properties of the NELOG indium phosphide layer are studied using atomic force microscopy, cathodoluminescence and room temperature mu-photoluminescence (mu-PL) measurements. Metal organic vapor phase epitaxial growth of InGaAsP/InP MQWs on the NELOG indium phosphide is conducted. The mask patterns to avoid loading effect that can cause excessive well/barrier thickness and composition change with respect to the targeted values is optimized. Cross-sectional transmission electron microscope studies show that the coalesced NELOG InP on Si is defect-free. PL measurement results indicate the good material quality of the grown MQWs. Microdisk (MD) cavities are fabricated from the MQWs on ELOG layer. PL spectra reveal the existence of resonant modes arising out of these MD cavities. A mode solver using finite difference method indicates the pertinent steps that should be adopted to realize lasing.