Tailoring Hydrogel Sheet Properties Through Co-Monomer Selection in AMPS Copolymer Macromers

This study investigates hydrogels based on 2-Acrylamido-2-methyl-1-propanesulfonic acid sodium salt (AMPS) copolymers, incorporating N-hydroxyethyl acrylamide (HEA) and 3-sulfopropyl acrylate potassium salt (SPA). The addition of HEA and SPA is designed to fine-tune the hydrogels’ water absorption and mechanical properties, ultimately enhancing their characteristics and expanding their potential for biomedical applications. A copolymer of AMPS, 2-carboxyethyl acrylate (CEA) combined with methacrylic acid (MAA) as poly(AMPS-stat-CEA-stat-MAA, PACM), was preliminarily synthesized. CEA and MAA were modified with allyl glycidyl ether (AGE) through ring-opening, yielding macromers with pendant allyl groups (PACM-AGE). Copolymers poly(AMPS-stat-HEA-stat-CEA-stat-MAA) (PAHCM) and poly(AMPS-stat-SPA-stat-CEA-stat-MAA) (PASCM) were also synthesized and modified with AGE to produce PAHCM-AGE and PASCM-AGE macromers. These copolymers and macromers were characterized by 1H NMR, FT-IR, and GPC, confirming successful synthesis and functionalization. The macromers were then photocrosslinked into hydrogels and evaluated for swelling, water content, and mechanical properties. The results revealed that the PASCM-AGE hydrogels exhibited superior swelling ratios and water retention, achieving equilibrium water content (~92%) within 30 min. While the mechanical properties of HEA and SPA containing hydrogels show significant differences compared to PACM-AGE hydrogel (tensile strength 2.5 MPa, elongation 47%), HEA containing PAHCM-AGE has a higher tensile strength (5.8 MPa) but lower elongation (19%). In contrast, SPA in the PASCM-AGE hydrogels led to both higher tensile strength (3.7 MPa) and greater elongation (92%), allowing for a broader range of hydrogel properties. An initial study on drug delivery behavior was conducted using PACM-AGE hydrogels loaded with photosensitizers, showing effective absorption, release, and antibacterial activity under light exposure. These AMPS-based macromers with HEA and SPA modifications demonstrate enhanced properties, making them promising for wound management and drug delivery applications.