Investigations of the Carbonization Process of Hybrid Polymer Microspheres Using the TGA-EGA Method: Assessment of the Impact of Sulphanilic Acid on the Process
Journal of thermal analysis and calorimetry(2024)
摘要
The TGA-EGA technique was used to study the influence of sulphanilic acid (SA) on the carbonisation process of the hybrid terpolymeric precursors composed of methacrylamide, divinylbenzene, and trimethoxyvinylsilane. The pristine polymers were impregnated with saturated solution of SA, dried, and carbonized at 600 °C under N2 atmosphere. The characteristic properties of both the pristine hybrid polymers and the resulting carbons were based on FTIR, Raman, and PXRD analyses, which revealed the materials were composed of amorphous polymeric or carbon phase interpenetrated by silica/silicate disordered network. The porosimetric analysis showed the resulted carbons possessed homogeneous supermicropores with the average pore width of 0.7 nm and reduced number of mesopores compared to pristine precursors. From the TGA results, it was followed that impregnated polymers decomposed in two stages, instead of one like pristine precursors did. Moreover, IDT of impregnated polymers was reduced by about 100 °C, and their Tmax was increased by 2–5.5 °C. Their decomposition proceeded slower by 22–37
更多查看译文
关键词
Hybrid materials,Hybrid polymers,Hybrid carbons,TGA-EGA,Carbonisation,Sulphanilic acid
AI 理解论文
溯源树
样例
![](https://originalfileserver.aminer.cn/sys/aminer/pubs/mrt_preview.jpeg)
生成溯源树,研究论文发展脉络
Chat Paper
正在生成论文摘要