Simulation of TiN/Ti Multilayer Coating under the Impact of Multiple Particles Based on Cohesive Element

In order to investigate the damage behavior of TiN/Ti multilayer coating under multi-particle impact and the influence of impact angle on erosion resistance, the ABAQUS 2019 software and the cohesive element technology were used for simulation. The results showed that, during the impact process, the upper surface of the TiN layer that was directly below the impact center was mainly subjected to compressive stress, while the lower surface was subjected to tensile stress. At the impact contact edge, tensile stress appeared on the upper surface of the TiN layer, while compressive stress appeared on the lower surface. The increase in the number of impacts leads to an increase in the maximum S11 stress inside the coating and the maximum displacement of the impact center during the impact process. The plastic damage was greater at the locations with higher strain in the Ti sublayer. During the impact process, severe damage occurred in both the top TiN layer and interface areas, and material failure occurred in the impact area. The increase in impact angle leads to an increase in the plastic strain energy of the entire model after the impact and the maximum S11 stress inside the coating during the impact process.