Bionic Structure and Biocompatibilities of Long Chain Branched Poly(l-Lactic Acid) Oriented Microcellular Foaming Material.

In order to solve the problem of uneven microporous structure of Poly(L-lactic acid) (PLLA) bulk orientation by using biological safety multi-functional plant oil as chain extenders (CE), multi -armed flexible chains were introduced into PLLA through reactive processing to prepare long chain branched PLLA (LCB-PLLA). When the total content of the CE was 6.15 wt%, PLLA and the CE reacted most fully, while maintaining the tensile strength of PLLA and improving toughness. After introducing the LCB structure, the presence of multi -armed flexible chains increased the mobility of the molecular chains, resulting in a significantly lower degree of crystallinity. When the draw ratio up to 900 %, the crystallinity of LCB-PLLA-F-900 % was only 45.15 %, lower than that of PLLA-F-900 %. Thanks to the mobility of polymer chains can be enhanced, which reduces the degree of crystallinity while promoting the uniform growth of oriented microporous structures. Finally, an oriented microporous biomimetic LCB-PLLA material with an average cell diameter of 540 nm was prepared, and the results of in vitro cell culture showed that the oriented micro-porous LCB-PLLA biomimetic material was more conducive to cell proliferation.