Recycling of Waste Glass and Incinerated Sewage Sludge Ash in Glass-Ceramics.

Disposal of waste glass and incinerated sewage sludge ash (ISSA) in landfills is a waste of resources and poses significant environmental risks. This work aims to recycle waste glass and ISSA together to form value-added glass-ceramics. The physical and mechanical properties, leaching behaviour, and microstructure of the glass-ceramics produced with different proportions of waste glass powder (WGP) and ISSA were investigated. Ther-modynamic calculations were performed to predict the formation of crystalline phases and the phase trans-formation involved. The results showed the potential of WGP and ISSA as raw materials in glass-ceramics production. WGP effectively densified the microstructure of the glass-ceramics by forming a viscous phase. As WGP content increased, the total porosity of glass-ceramics decreased whereas the density increased, accom-panied by the formed anorthite transforming into wollastonite. The incorporation of WGP densified and refined the pore structure of the glass-ceramics, thereby improving the mechanical properties and reducing the water absorption. The glass-ceramics produced with a 50:50 blend of WGP and ISSA exhibited the highest compressive strength of 43.7 MPa and the lowest water absorption of 0.3 %. All fabricated glass-ceramics exhibited innocuous heavy metal leaching. The co-sintering of ISSA and WGP can produce additive-free glass-ceramics, characterized by reduced energy consumption and notable heavy metal immobilization capacity. These materials hold promise for utilization in construction as building materials.