Evolution of interfacial voids in Cu-to-Cu joints
Materials Characterization(2022)
摘要
In this study, the Cu joints were fabricated by Cu pads with the highly (111)-oriented nano-twinned structure at 250 degrees C. We reported a new characterization approach by plan-view images of focused ion beam (FIB) to observe the evolution of interfacial voids in the Cu joints under annealing. The distribution function of interfacial voids and the kinetics of void evolution were then studied and analyzed. The evolution of interfacial voids was proposed to occur at different stages, which were dominant by plastic deformation, creep deformation, and void ripening caused by grain boundary and lattice diffusion. Significant void ripening was observed at early stage of bonding attributed to fast grain boundary diffusion. However, after the bonding interface was eliminated, the void sizes did not change due to slow lattice diffusion.
更多查看译文
关键词
Cu-to-Cu bonding technology,Interfacial voids,Void ripening,Interfacial elimination
AI 理解论文
溯源树
样例
生成溯源树,研究论文发展脉络
Chat Paper
正在生成论文摘要