Mussel-inspired Coating of α-AlH3: A Compact Structure with Highly Enhanced Stability

we present a novel surfacing coating to resolve the stability of α-AlH3. Inspired by the strong chemical adhesion of mussels, the polymerization of dopamine was first introduced to coat α-AlH3 through a simple situ polymerization. The α-AlH3 was used as a substrate. In-depth characterizations confirmed compact formation with PDA on α-AlH3 surface. The coated α-AlH3 sample was characterized by XRD XPS and SEM . The results show that a strong PDA film is formed on the surface of α-AlH3, the PDA@α-AlH3 retained primary morphology. The crystal form of α-AlH3 does not change after coated by PDA. The results of XPS analysis show that N1s appears on the material after coated by PDA, indicating that polydopamine is formed on the surface of α-AlH3. The moisture absorption tests show that the moisture absorption rate of α-AlH3 is greatly reduced after being coated with PDA. The excellent intact ability of PDA prevent α-AlH3 reacting with watered in the air. The thermal stability of α-AlH3 before and after coating was analyzed by DSC. This work demonstrates the successful applications of dopamine chemistry to α-AlH3, thereby providing a potential method for the metastable materials.