Effect of Temperature on the Corrosion Behavior and Corrosion Resistance of Copper-Aluminum Laminated Composite Plate

In this paper, the effect of temperature on the corrosion behavior and corrosion resistance of the copper-aluminum laminated composite plates were investigated by salt-spray corrosion, potential polarization curve and electrochemical impedance spectroscopy. Moreover, the microstructure of the copper-aluminum laminated composite plate after salt-spray corrosion was observed by scanning electron microscope, and X-ray photoelectron spectroscopy was used to study the composition of corrosion product. The results revealed that the corrosion products of the copper-aluminum laminated composite plate were Al2O3 and AlOOH. Due to the galvanic corrosion of the copper-aluminum laminated composite plate, the cathode underwent oxygen absorption corrosion during the corrosion process; therefore, the presence of moisture and the amount of dissolved oxygen in the corrosive environment had a great influence on the corrosion process. The increasing temperature would evaporate a large amount of moisture, resulting in the corrosion product-aluminum oxide dehydrated and covered the surface of the material in the process of salt-spray corrosion, which played a role in protecting the material. Therefore, the corrosion resistance of the copper-aluminum laminated composite plate first decreased and then increased. In the salt-spray corrosion environment, the corrosion resistance of the copper-aluminum laminated composite plate reached the lowest at 45 degrees C, and its corrosion rate was the fastest, at 0.728 g/m(2)center dot h. The electrochemical corrosion occurred in the solution, and the impact was small; however, in addition to the protective corrosion products, the ion mobility in the solution also had a certain influence on the corrosion rate, and the ionic activity increased with the increase of temperature. Therefore, the corrosion resistance of the copper-aluminum laminated composite plate gradually decreased as the temperature increased, and its corrosion resistance was the worst at 50 degrees C.