Fabrication and characterization of magnesium scaffold using different processing parameters

Structural and mechanical properties of scaffolds are important for hard tissue reconstruction. In this study, magnesium scaffolds were fabricated using space holder method for bone tissue reconstruction and the effect of cold compaction pressure and also volume percent of porosity on structural and mechanical properties of scaffolds were investigated using scanning electron microscopy (SEM) and uniaxial compression test. The carbamide spacer agent was also removed after pellet compaction, using NaOH solution and ethanol for the first time and their effect on phases present in scaffold after sintering was investigated using x-ray diffraction (XRD) analysis. Based on the results of mechanical and structural assessments, the optimum cold compaction pressure was selected 350 MPa for pellet compaction. The elastic modulus and strength of magnesium scaffolds including 67 vol.% porosity were in the range of 0.20-0.28 GPa and 4-4.25 MPa, respectively which is comparable to cancellous bone tissue. The mechanical properties of magnesium scaffolds decreased by increasing the porosity. The results also revealed that ethanol is a more suitable liquid for carbamide removal compared to NaOH solution.