The Effect of Laser Scanning Speed on Microstructural Evolution During Direct Laser Deposition 12crni2 Alloy Steel

This paper focused on the effect of different laser scanning speed (4 mm/s, 5 mm/s, 6 mm/s and 7 mm/s) on the microstructural evolution of direct laser deposition (DLD) 12CrNi2 alloy steel, and analyzed the relationship between microstructure and performance of DLD-processed samples. The results showed that the microstructure in the middle of as-deposited samples consisted of a large amount of bainite, a small amount of martensite (M) and ferrite (F). With the increase of laser scanning speed, the fraction of ferrite decreased from 55.6% to 14.7%, while that of martensite increased from nearly 0% to 4.9%. Besides, as increasing the laser scanning speed, granular bainite (GB) transformed into lath bainite (13) due to the increase of cooling rate, and the fraction of LB reached the maximum of 29.9% when the scanning speed was 7 mm/s. In addition, the functions about the relationship between laser scanning speed and phase fractions were fitted in order to provide a theoretical basis for the design of DLD process parameters. EBSD maps of as-deposited samples exhibited anisotropy due to the complex heat flux direction during the multi-layer laser deposition process. With the increase of laser scanning speed, the grain size showed a downward trend from 5.89 mu m(2) to 3.44 mu m(2). The sample fabricated at 7 mm/s contained more LB and M, leading to the highest mean microhardness of 355 +/- 6 HV0.2. The sample fabricated at 6 mm/s exhibited the best wear resistance due to its optimum combination of hardness and toughness. Because of a large amount of ferrite with optimal toughness, the sample fabricated at 4 mm/s had the best impact toughness of a(ku) = 80 J/cm(2).