Effect of Final Electromagnetic Stirring on Solidification Microstructure of GCr15 Bearing Steel in Simulated Continuous Casting
Journal of Iron and Steel Research International/Journal of iron and steel research, international(2019)
摘要
The effect of final electromagnetic stirring on the solidification structure, element segregation, and carbides of GCr15 bearing steel was investigated. The experiment of continuous casting of the steel was carried out by using a continuous casting physical simulation apparatus with the final electromagnetic stirring. The liquid core profile was revealed by the pour-out method during the solidification process. Eight ingots were produced under different electromagnetic stirring parameters for comparison. The results show that, at the final stage of solidification, intense electromagnetic stirring exacerbates the central carbon segregation, resulting in more serious precipitation of the primary carbides. It is also found that the carbides in the segregation area are dominantly M 3 C type, together with a small amount of M 7 C 3 -type and M 3 C 2 -type carbides. In this physical simulation model, the optimal stirring parameters to obtain a fine and homogeneous structure are the liquid pool width of 15 mm, current intensity of 150 A, and stirring frequency of 5 Hz.
更多查看译文
关键词
GCr15 bearing steel,Solidification structure,Continuous casting,Final electromagnetic stirring,Segregation,Carbide
AI 理解论文
溯源树
样例
生成溯源树,研究论文发展脉络
Chat Paper
正在生成论文摘要