Fabrication, Electrochemical and Catalytic Properties of the Nanocomposites Composed of Phosphomolybdic Acid and Viologen-Functionalized Multi-Walled Carbon Nanotubes

Electroactive nanocomposites composed of phosphomolybdic acid (PMA) and viologen-functionalized carbon nanotubes were synthesized and used as heterogeneous catalysts for the electrocatalytic reduction of bromate. Viologen (V) was first covalently anchored on the surface of multi-walled carbon nanotubes (MWNTs) to produce positively charged MWNT-V polyelectrolyte, which was then combined with PMA through electrostatic interaction to form MWNT-V@PMA nanocomposites. Thermogravimetric analysis revealed that the organic species in the MWNT-V polyelectrolyte was about 30% in weight. Composition, structure, and morphology of the nanocomposites were investigated by using UV-vis, infrared, Raman and X-ray photoelectron spectroscopy as well as field emission transition electron microscope. The thickness of organic substituents, viologen, and PMA in the nanocomposites was approximately 10 nm covered on the surface of MWNTs. Cyclic voltammogram measurements for the casting films of MWNT-V@PMA nanocomposites revealed four couples of redox waves with cathodic potentials at about −0.56, −0.19, 0.02, 0.21 V, and anodic ones at about −0.46, −0.11, 0.12, 0.31 V (vs Ag/AgCl), respectively, among which the first one corresponded to the electron transfer process of viologens and others to that of the PMA adsorbed. Finally, the MWNT-V@PMA modified electrodes were used as heterogeneous catalysts for the electrocatalytic bromate reduction, which revealed an almost linear correction between the current density and the bromate concentrations in the concentration range from 1 to 15 mmol/l.