[Influence of Reaction Time on Titanate Nanomaterials and Its Adsorptioi Capability for Lead in Aqueous Solutions].

Titanate nanomaterials (TNs) were synthesized via a simple hydrothermal method using TiO2 (ST-01) and NaOH as the raw materials, and presented different morphologies by adjusting the reaction time. The physico-chemical properties of the as-prepared TNs, such as morphology, structure, surface area, and chemical composition were characterized by XRD, SEM and BET. The adsorption capability and rules of Pb(II) in aqueous solutions were tested in the static system. The results showed that the TNs prepared with 12-72 h reaction time were pure monoclinic phase titanate and their specific surface areas were in the range from 243.05 m2 x g(-1) to 286.20 m2 x g(-1). TNs with reaction time between 12-36 h mainly showed sheet structure, and those with reaction time higher than 48 h showed linear structure. The adsorption capacity of Pb(II) by TNs-12, TNs-24, TNs-36, TNs-48, TNs-60 and TNs-72 was 479.40, 504.12, 482.00, 388.10, 364.60 and 399.00 mg x g(-1), respectively. The sheet TNs had a better adsorption capacity than the linear TNs. TNs-24 had the highest adsorbing capacity. The adsorption kinetics of Pb(II) by TNs-24 followed the pseudo-second-order model, and the equilibrium data was best fitted with the Langmuir isotherm model. The equilibrium adsorption time of TNs-24 was 120 min, and the adsorption was an exothermic process, with a high adsorption capacity at low temperature or room temperature; the optimal adsorption pH was 5.0. When pH was 1.0, the desorption rate of TNs-24 could reach 99.00%, and the removal efficiency of Pb(II) by regenerated TNs was still more than 97% after six times of usage. Therefore, TNs could efficiently remove Pb(II) in aqueous solutions, and the optimal reaction time should be controlled to 12-24 h. When Cd(II) or Ni(II) existed in the solution, the equilibrium adsorption capacity and removal rate of TNs-24 were decreased. The adsorption mechanism was mainly ion-exchanged between Pb(II) and H+/Na+ in TNs.