Long-term Thermal Stability of Ti/Al/Mo/Au Ohmic Contacts on N-Gan

Improved performance of the ohmic contacts on n-GaN has been demonstrated with the use of MoAu as the capping layer on TiAl metallization. Contact resistance as low as 0.13 Θ-mm was achieved in these ohmic contacts when annealed at 850°C for 30 sec. We have studied the long-term thermal stability of these contacts at 500°C, 600°C, 750°C, and 850°C, respectively. The Ti/Al/Mo/Au metallization forms low contact-resistance ohmic contacts on n-GaN that are stable at 500°C and 600°C after 25 h of thermal treatment. The ohmic-contact performance degrades after 10 h of thermal treatment at 750°C, while the contacts exhibit nonlinear current-voltage (I-V) characteristics after 1 h of thermal treatment at 850°C with the formation of oxide on the surface of the contacts accompanied by surface discoloration. The intermetallic reactions taking place in the contacts during the long-term thermal treatments were studied using Auger electron spectroscopy (AES), and the surface morphology was characterized using atomic force microscopy (AFM).