Long-Term, Cyclic Oxidation Behaviour of Alumina- and Chromia-Forming Alloys
Defect and Diffusion Forum(2005)
摘要
The oxidation resistance behaviour of a number of surface-treated FeCrAl commercial alloys and some model alloys of well-defined composition, incorporating a range of reactive elements in trace amounts, has been studied under thermal cyclic conditions in air with and without additions of water vapour. Additions of reactive elements such as Zr, La, Y, Hf modify the oxidation resistance behaviour of FeCrAl-alloys by improving the scale adherence and consequently may extend the lifetime of FeCrAl steels. The presence of the water vapour can affect oxidation in a number of different ways. Our results may indicate that high content of water vapour can cause the lives of such alloys to be decreased. This work forms part of a larger European-funded project to evaluate physical properties, microstructural features, oxidation/corrosion resistance and lifetime improvement. The correlation between alloy parameters and lifetime; as well as the modeling of oxide scale behaviour as function of cycling conditions is also studied.
更多查看译文
关键词
FeCrAl steels,oxidation/corrosion resistance,coatings,aluminium enrichment
AI 理解论文
溯源树
样例
生成溯源树,研究论文发展脉络
Chat Paper
正在生成论文摘要