Aging Treatment Induces the Preferential Crystallographic Orientation of Αs in the Near-α Titanium Alloy Ti60
Metals(2024)
摘要
In this article, we subjected the Ti60 alloy to solid-solution treatment at 1020 °C and aging treatment at 600 °C, respectively, achieving a bimodal microstructure. The microstructures obtained after aging treatment showed no significant difference in the primary α-phase content, size, and width of the lamellar α phase. This suggests that the final microstructure morphology is primarily determined by the solid-solution temperature, with the aging process exerting less pronounced effects on microstructural alterations. Furthermore, we investigated the effect of solid-solution and aging treatment on the crystallographic orientation evolution of the secondary α phase (αs) in the near-α titanium alloy Ti60. The αs phase displays a random orientation in solid-solution treatment sample, while it demonstrated a preferential {0 1 −1 0} orientation after aging treatment. This interesting phenomenon is attributed to the enhanced variant selection resulting from the dissolution of variant near 60° and 90° during aging. Furthermore, the αs with {0 1 −1 0} orientation nucleated at the grain boundary and coalesced into larger αs lath with increasing aging time, further contributing to the αs {0 1 −1 0} texture.
更多查看译文
关键词
near-alpha titanium alloys,secondary alpha phase(alpha(s)),variant selection,aging treatment
AI 理解论文
溯源树
样例
![](https://originalfileserver.aminer.cn/sys/aminer/pubs/mrt_preview.jpeg)
生成溯源树,研究论文发展脉络
Chat Paper
正在生成论文摘要