Anisotropic Foams Derived from Textile-Based Cellulose Nanocrystals and Xanthan Gum

The upcycling of discarded garments can help to mitigate the environmental impact of the textile industry. Here, we fabricated hybrid anisotropic foams having cellulose nanocrystals (CNCs), which were isolated from discarded cotton textiles and had varied surface chemistries as structural components, in combination with xanthan gum (XG) as a physical crosslinker of the dispersion used for foam preparation. All CNCs had crystallinity indices above 85 %, zeta potential values below -40 mV at 1 mM NaCl, and true densities ranging from 1.61 to 1.67 g center dot cm(-3). Quartz crystal microbalance with dissipation (QCM-D) measurements indicated weak interactions between CNC and XG, while rheology measurements showed that highly charged CNCs caused the XG chains to change from an extended to a helicoidal conformation, resulting in changes the in viscoelastic properties of the dispersions. The inclusion of XG significantly enhanced the compression mechanical properties of the freeze-casted foams without compromising their thermal properties, anisotropy, or degree of alignment. CNC-XG foams maintained structural integrity even after exposure to high humidity (91 %) and temperatures (100 degrees C) and displayed very low radial thermal conductivities. This research provides a viable avenue for upcycling cotton-based clothing waste into high-performance materials.