Electrospinning/3D printing drug-loaded antibacterial polycaprolactone nanofiber/sodium alginate-gelatin hydrogel bilayer scaffold for skin wound repair

Skin injuries and defects, as a common clinical issue, still cannot be perfectly repaired at present, particularly large-scale and infected skin defects. Therefore, in this work, a drug-loaded bilayer skin scaffold was developed for repairing full-thickness skin defects. Briefly, amoxicillin (AMX) was loaded on polycaprolactone (PCL) nanofiber via electrospinning to form the antibacterial nanofiber membrane (PCL-AMX) as the outer layer of scaffold to mimic epidermis. To maintain wound wettability and promote wound healing, external human epidermal growth factor (rhEGF) was loaded in sodium alginate-gelatin to form the hydrogel structure (SG-rhEGF) via 3D printing as inner layer of scaffold to mimic dermis. AMX and rhEGF were successfully loaded into the scaffold. The scaffold exhibited excellent physicochemical properties, with elongation at break and tensile modulus were 102.09 ± 6.74 % and 206.83 ± 32.10 kPa, respectively; the outer layer was hydrophobic (WCA was 112.09 ± 4.67°), while the inner layer was hydrophilic (WCA was 48.87 ± 5.52°). Meanwhile, the scaffold showed excellent drug release and antibacterial characteristics. In vitro and in vivo studies indicated that the fabricated scaffold could enhance cell adhesion and proliferation, and promote skin wound healing, with favorable biocompatibility and great potential for skin regeneration and clinical application.