Low-Temperature Phase Formation in the BaF2–LaF3 System

Barium lanthanum fluoride powders have been prepared by reacting barium nitrate and lanthanum nitrate in molten sodium nitrate at 350 and 450°C, using a sodium fluoride as a fluorinating agent. A fivefold excess of sodium fluoride has been shown to prevent pyrohydrolysis. We have identified a phase of variable composition with the fluorite structure, Ba1–xLaxF2+x (0.3 < x < 0.5), which has high ionic conductivity (2.3 × 10–4 S/cm at 500 K) and an activation enthalpy for ionic transport of 0.50 ± 0.01 eV.