Applications of polymer coatings consisting of 9,9′-(4,4′-sulfonylbis(4,1-phenylene))biscarbazole and thiophene derivatives in electrochromic devices
PROGRESS IN ORGANIC COATINGS(2023)
摘要
A carbazole derivative (9,9′-(4,4′-sulfonylbis(4,1-phenylene))biscarbazole (SpDc)) was synthesized; subsequently, P(SpDc), P(SpDc-co-TP), P(SpDc-co-MTP), P(SpDc-co-PTP), and P(SpDc-co-HTP) films were electrochemically coated on ITO/glass substrates. Electrochromic characterizations show that the P(SpDc) film is pale ochre, dark khaki, moss green, and dark olive green at 0.0, 0.8, 1.0, and 1.1 V, respectively. The square wave potential step absorptiometry of the polymeric coatings shows that the P(SpDc-co-PTP) film exhibits a high transmittance change (ΔT = 52.8%) and a moderate coloration efficiency (η = 120.8 cm2 C−1). Furthermore, dual-layer electrochromic devices (ECDs) were fabricated using P(SpDc), P(SpDc-co-TP), P(SpDc-co-MTP), P(SpDc-co-PTP), and P(SpDc-co-HTP) as anodic coatings and PProDOT-Bz2 as the cathodic coating. P(SpDc-co-TP)/PProDOT-Bz2 ECD exhibited multicolored electrochromism, a high ΔT (50.9% at 635 nm), a high η (820.5 cm2 C−1 at 635 nm), and a fast switching time (less than 0.1 s). Given the adequate electrochromic performance of the organic coatings, it can be inferred that these coatings could be used in promising organic ECD applications.
更多查看译文
关键词
Organic coating,Electrochromic electrode,Multicolor electrochromism,Transmittance change,Organic electrochromic device
AI 理解论文
溯源树
样例
![](https://originalfileserver.aminer.cn/sys/aminer/pubs/mrt_preview.jpeg)
生成溯源树,研究论文发展脉络
Chat Paper
正在生成论文摘要