Texture and High Yield Strength of Rapidly Solidified AZ31 Magnesium Alloy Extruded at 250 C
Materials (Basel, Switzerland)(2023)
摘要
In this study, commercial AZ31B magnesium alloy was used to compare the differences between the microstructure, texture, and mechanical properties of conventional solidification (as homogenized AZ31) and rapid solidification (as RS AZ31). The results demonstrate that a rapidly solidified microstructure leads to better performance after hot extrusion with a medium extrusion rate (6 m/min) and extrusion temperature (250 degrees C). The average grain size of as-homogenized AZ31 extruded rod is 100 mu m after annealing and 4.6 mu m after extrusion, respectively, but that of the as-RS AZ31 extruded rod is only about 5 mu m and 1.1 mu m, correspondingly. The as-RS AZ31 extruded rod attains a high average yield strength of 289.6 MPa, which is superior to the as-homogenized AZ31 extruded rod, and is improved by 81.3% in comparison. The as-RS AZ31 extruded rod shows a more random crystallographic orientation and has an unconventional weak texture component in < 1121 >/< 2021 > direction, which has not been reported yet, while the as-homogenized AZ31 extruded rod has an expected texture with prismatic < 1010 >/< 1210 >//ED.
更多查看译文
关键词
hot-extruded AZ31 alloy,rapid solidification powder metallurgy,mechanical property,grain refinement,unusual texture
AI 理解论文
溯源树
样例
![](https://originalfileserver.aminer.cn/sys/aminer/pubs/mrt_preview.jpeg)
生成溯源树,研究论文发展脉络
Chat Paper
正在生成论文摘要