Near-infrared Photoluminescence Radiation from the Interface of an Annealed ZnO Nano Thin Film/silicon Heterostructure Array
Optical materials(2023)
摘要
In this study, the photoluminescence (PL) features of an annealed ZnO nano thin film/silicon heterostructure array were investigated. PL spectra were observed, which were closely related to the annealing temperature and covered visible-near infrared (NIR) region among 500-900 nm (1.37 eV-1.59 eV), especially two unexpected NIR peaks at 1.44 eV, 1.57 eV were detected. silicon array was synthesized by hydrothermal corrosion by using the solution composed of ferric nitrate and hydrofluoric acid. A regular array surface was obtained and exhibited a red PL emission with a slight position shift as the excitation wavelength varied. Oxygen defects in the array structure and silicon nanoparticles were responsible for the red PL. ZnO nano thin film/silicon heterostructure array was prepared by heating the Zn film coated array, which was obtained by magnetron sputtering. As the heating temperature increased to 350-400 degrees C, the PL intensity of the ZnO nano thin film/silicon heterostructure array decreased to approximately half that of the original, and the orange-red PL peaks was substituted by NIR radiations gradually. The models of electrons transition at the interface were analyzed to explain the emissions. The results demonstrated that the potential of ZnO/silicon heterostructure array as a NIR-emitting material.
更多查看译文
关键词
Photoluminescence,Near infrared emission,Interface,Silicon array,Zinc oxide
AI 理解论文
溯源树
样例
![](https://originalfileserver.aminer.cn/sys/aminer/pubs/mrt_preview.jpeg)
生成溯源树,研究论文发展脉络
Chat Paper
正在生成论文摘要