Morphological Characteristics of Bamboo Panel Milling Dust Derived from Different Average Chip Thicknesses

The massive amounts of dust formed during bamboo CNC milling presents serious risks to human health and equipment. The present study aimed to determine the particle size distribution (PSD) and shape characteristics of bamboo milling dust derived from different average chip thicknesses. Spindle speed and feed rate were varied in combination, in setting up two experimental groups having the same average chip thicknesses. Sieving and flatbed scanning image analyses were collectively utilized for the morphological analysis of bamboo dust. The results showed that less than 5% of the particles were below 100 mu m in terms of mass, but represented more than 83% in number. Average chip thickness was positively correlated with a mass proportion of bamboo dust with large size, which was preferably generated when reducing spindle speed instead of increasing feed rate. Spindle speed and feed rate individually affected the particle size and particle size distribution instead of average chip thickness. The aspect ratio, roundness and convexity of bamboo milling dust were augmented with a reduction in particle size, indicating that bamboo milling dust with smaller size had more a regular shape, a smoother profile and fewer corners. These findings provide a theoretical basis for better understanding bamboo milling dust and its related control in the bamboo processing industry.