Research of a novel double cross-linking fracturing fluid

A kind of JDL-1 thickener for betaine hydrophobic association polymer was prepared by aqueous solution polymerization of mixed micelles, AM, AA, AMPS and DM16 were used as raw materials, which was synthesized by redox initiator system. Friction tester and high-temperature rheometer were used to evaluate the resistance reduction and temperature and shear resistance of the thickener. The results show that the viscosity average molecular weight of the polymer prepared with AM, AA, AMPS and DM16 mass ratio of 70∶20∶5∶5 was higher than 12 million, and the dissolution time of the polymer was less than 3 min. When the surfactant is used for physical cross-linking, the apparent viscosity of the cross-linked fracturing fluid is larger than that of 60 mPa·s at 90 °C, 170 s-1 sheared 1 h; when metal cross-linking agent is used for coordination cross-linking, the apparent viscosity is larger than that of 80 mPa·s at 120 °C, 170 s-1 sheared 1 h. The drag reduction rate was 73%, the anti-swelling rate was higher than70%, and the damage rate was less than10%. The field trial was successful and confirmed the multifunctional effect of betaine-type hydrophobic associating polymer.