Fabrication And Compressive Properties Of Open-Cell Ni-Mo-Cr (Hastelloy) Foams Manufactured By Electrostatic Powder Spraying
ARCHIVES OF METALLURGY AND MATERIALS(2020)
摘要
An open-cell Ni-Mo-Cr foam was newly manufactured using electrostatic powder spraying process and its room-temperature compressive properties were investigated in this study. For manufacturing Ni-Mo-Cr foam, Ni-Mo-Cr powders were sprayed on the polyurethane pre-form by electrostatic powder spraying process. And then, Ni-Mo-Cr powder sprayed pre-forms were sintered at 1200 degrees C, 1250 degrees C, and 1300 degrees C, respectively. The relative densities of Ni-Mo-Cr foams were measured at 4 similar to 5%. Room temperature compressive curves of ESP Ni-Mo-Cr foams represented the typical compressive 3-stages (elastic, plateau, densification) of open-cell metallic foam. As a result of observation of deformed specimen, the fracture mode found to be changed from brittle to ductile as sintering temperature increased. Based on these findings, correlations between structural characteristics, microstructure, and compressive deformation behavior were also discussed.
更多查看译文
关键词
metallic foam, electrostatic powder spraying, Ni-Mo-Cr alloy, sintering, compressive property
AI 理解论文
溯源树
样例
生成溯源树,研究论文发展脉络
Chat Paper
正在生成论文摘要