Co-electrodeposited Porous Poplar Flower-Like Poly(hydroxymethyl-3,4-ethylenedioxythiophene)/peg/ws2 Hybrid Material for High-Performance Supercapacitor

The morphology of electrode material is generally critical to affecting their electrochemical performance. Here, a porous poplar flower-like PEDOT-MeOH/PEG/WS2 hybrid material is successfully prepared using a simply co-electrodeposition method. With the assistance of poly(ethylene glycol) (PEG), the chemically exfoliated WS2 nanosheets are doped into poly(hydroxymethyl-3,4-ethylenedioxythiophene) (PEDOT-MeOH) film. The formation of a porous poplar flower-like PEDOT-MeOH/PEG/WS2 composite is proved by scanning electron microscopy, transmission electron microscopy, infrared spectra, energy-dispersive X-ray spectrometry and Xray photoelectron spectroscopy. The maximum capacitance of the composite reaches 461.5 mF cm(-2), which is 1.6 times greater than that of PEDOT-MeOH/PEG film. As-fabricated PEDOT-MeOH/PEG/WS2 composite can keep 85.8% of the initial areal capacitance after 5000 cycles. Additionally, PEDOT-MeOH/PEG/WS2-based symmetrical supercapacitor presents a capacitive capacity of 62.7 mF cm(-2) at 0.5 mA cm(-2), specific energy of 8.72 x 10(3) mu Wh cm-2 at 2.62 x 10(5) mu W cm(-2), and capacitive retention of 83.3% after 5000 cycles with a 100% coulombic efficiency. The capacitance improvement of PEDOT-MeOH/PEG/WS2 composite is closely related to porous poplar flower-like structure as well as the cooperation-enhancing effect between PEDOTMeOH and WS2. These results imply that PEDOT-MeOH/PEG/WS2 composite will have great potential application in the field of the energy storage.