Preparation of ThO 2 as a Structural Analogue for Nuclear Fuel via Surfactant-Templated Sol-Gel Route
semanticscholar(2019)
摘要
Received: 21 January 2019 Revised: 25 January 2019 Accepted: 31 January 2019 Available online: 14 February 2019 K E Y W O R D S Sol-gel synthesis of surfactant-templated nanostructured ceramic materials is usually carried out via controlled hydrolysis and condensation of a starting material in the presence of micelles of a polymer, followed by its removal by extraction or calcination. In this work, surfactant template sol-gel route for the synthesis of thorium dioxide gels using thorium nitrate and octyl phenol ethoxylate polymer as a structure directing agent was described, and the sinter ability of the produced ThO2 powder (ThO2-S) was investigated in comparison with commercial one (ThO2-C). Prepared ThO2-S composed of micro and meso pores and exhibited high surface area as 31.23 m2/g and particle size as 15.1 nm. The produced powder ThO2-S was pressed and sintered to form the high density ThO2 pellet. The final grain size of the pellets reached below micrometer size. The calculated green and sintered densities of the fabricated pellets, and their microstructural characteristics studies, utilizing SEM images, show that this synthesizing route yielded a good sinter ability of the synthesized ThO2 Nano powder at low temperature. Prepared ThO2-S sample and commercial ThO2 were sintered under the atmospheres “Ar” and “Ar8%H2, and comparison of data from samples sintered under the both of two different atmospheres at 1500 °C, show that the atmosphere had no effect on density value. Furthermore, the green density of ThO2-S pellets is less than ThO2-C but the pellets which were fabricated from the ThO2-S have reached better sintered density than the pellets fabricated by ThO2-C. ThO2 Sol gel Process Fuel pellet Density Sinter ability G R A P H I C A L A B S T R A C T
更多查看译文
AI 理解论文
溯源树
样例
![](https://originalfileserver.aminer.cn/sys/aminer/pubs/mrt_preview.jpeg)
生成溯源树,研究论文发展脉络
Chat Paper
正在生成论文摘要