Enhancing Piezoelectric Coefficient with High Curie Temperature in BiAlO3-modified BiFeO3–BaTiO3 Lead-Free Ceramics
SOLID STATE SCIENCES(2019)
摘要
In this work, the lead-free piezoelectric ceramic (1-x)[0.65Bi(1.05)FeO(3)-0.35BaTiO(3)] - xBiAlO(3), (BFBT-xBA) (where x = 0, 0.010, 0.015, 0.020, 0.025, and 0.030), were synthesized by a solid-state reaction method, followed by air quenching process. The effects of BiAlO3 (BA) on the crystal structure, morphology and electrical properties of 0.65B(1.05)FeO(3)-0.35BaTi(3) (BF-BT) ceramics have been investigated. With the incorporation of BA-content (x = 0.010) the coexistence of rhombohedral and pseudocubic phases were observed. Scanning electron microscope (SEM) micrographs revealed that the average grain size of BF-35BT ceramics increased with the addition of BA. Well-saturated ferroelectric (P-E) hysteresis loops with definite remnant polarization (P-r) and coercive field (E-c) were observed. As a result, improvements in ferroelectric and piezoelectric properties with relative high Curie temperature (T-C) were obtained at the optimum composition (x = 0.010). In addition, the static piezoelectric coefficient (d(33)) was enhanced from 97 pC/N for the base composition (x = 0) to 210 pC/N for the optimum (x = 0.010) composition.
更多查看译文
关键词
Piezoelectric,Lead-free,Dielectric,Ferroelectric,BiFeO3-BaTiO3
AI 理解论文
溯源树
样例
![](https://originalfileserver.aminer.cn/sys/aminer/pubs/mrt_preview.jpeg)
生成溯源树,研究论文发展脉络
Chat Paper
正在生成论文摘要