Stability of colloidal ZSM-5 catalysts synthesized in fluoride and hydroxide media

ZSM-5 zeolite crystals with carefully controlled thicknesses in the range 20–110 nm, i.e. in the colloidal domain, were synthesized in fluoride and hydroxide media. The crystals were treated in steam at high temperature to evaluate the stability and evaluated by SEM, XRD, NMR and NH3-TPD. The results showed that the framework of crystals synthesized in fluoride media was more stable than the framework of crystals synthesized in hydroxide media. This should be an effect of lower concentration of structural defects and silanol groups in the former zeolites as reported by other groups. However, independently of the synthesis conditions, all crystals dealuminated rapidly when treated with steam at the conditions investigated in the present work.