Growth Temperature Optimization of GaAs-based In0.83Ga0.17As on InxAl1−xAs Buffers

Improved quality of gas source molecular beam epitaxy grown In0.83Ga0.17As layer on GaAs substrate was achieved by adopting a two-step InxAl1-xAs metamorphic buffer at different temperatures. With a high-temperature In0.83Al0.17As template following a low-temperature composition continuously graded InxAl1-xAs (x = 0.05-0.86) buffer, better structural, optical and electrical properties of succeeding In0.83Ga0.17As were confirmed by atomic force microscopy, photoluminescence and Hall-effect measurements. Cross-sectional transmission electron microscopy revealed significant effect of the two-step temperature grown InAlAs buffer layers on the inhibition of threading dislocations due to the deposition of high density nuclei on GaAs substrate at the low growth temperature. The limited reduction for the dark current of GaAs-based In0.83Ga0.17As photodetectors on the two-step temperature grown InxAl1-xAs buffer layers was ascribed to the contribution of impurities caused by the low growth temperature of InAlAs buffers. (C) 2018 Elsevier B.V. All rights reserved.