Large thermoelectric power factors and impact of texturing on the thermal conductivity in polycrystalline SnSe
Journal of Materials Chemistry C(2016)
摘要
Single crystals of SnSe have been reported to have very high thermoelectric efficiencies with a maximum figure merit zT = 2.5. This outstanding performance is due to ultralow thermal conductivities. We report on the synthesis of highly textured polycrystalline SnSe ingots with large single-crystal magnitude power factors, S-2/rho = 0.2-0.4 mW m(-1) K-2 between 300-600 K, increasing to 0.9 mW m(-1) K-2 at 800 K, and bulk thermal conductivity values kappa(300K) = 1.5 W m(-1) K-1. However, small SnSe ingots, which were measured in their entirety, were found to have a substantially reduced kappa(300K) = 0.6 W m(-1) K-1. Microscopy and diffraction revealed two distinct types of texturing within the hot-pressed ingots. In the interior, large coherent domains of SnSe platelets with a similar to 45 degrees orientation with respect to the pressing direction are found, while the platelets are preferentially oriented at 90 degrees to the pressing direction at the top and bottom of the ingots. Fitting the kappa(T) data suggests an increase in defect scattering for the smaller ingots, which is in keeping with the presence of regions of structural disorder due to the change in texturing. Combining the measured S-2/rho with the bulk ingot kappa values yields zT = 1.1 at 873 K.
更多查看译文
关键词
thermal conductivity,polycrystalline snse,large thermoelectric power factors
AI 理解论文
溯源树
样例
![](https://originalfileserver.aminer.cn/sys/aminer/pubs/mrt_preview.jpeg)
生成溯源树,研究论文发展脉络
Chat Paper
正在生成论文摘要