Grain Refinement of AZ61 Alloy after ECAP Processing
Materials Science Forum(2017)
摘要
Electron microscopy techniques were used to characterize the microstructure and deformation behavior of AZ61 alloy proceeded by ECAP. The commercial AZ61 alloy subjected to severe plastic deformation possesses a two-phase microstructure consisting of solid solution matrix and massive γ-phase Mg17Al12, or Mg17(Al,Zn)12 distributed mostly at grain boundaries. Based on selected area diffraction and electron back scattered diffraction applied to a sample after the third pass, it can be concluded that plastic deformation induced by ECAP occurs mainly by slip mode forming a high density network of dislocation inside the grains. The grains size was significantly refined to 1.4 μm after the third pass of ECAP. The refinement of grain size is probably due to polygonization process associated with formation of high angle grain boundaries due to dislocations rearrangement. (Al, Zn)12Mg17 precipitates of size scattered from 100 to 200 nm and also the primary precipitates of Al6Mn phase were observed in this alloy.
更多查看译文
关键词
az61 alloy,grain
AI 理解论文
溯源树
样例
![](https://originalfileserver.aminer.cn/sys/aminer/pubs/mrt_preview.jpeg)
生成溯源树,研究论文发展脉络
Chat Paper
正在生成论文摘要