Effect of Rapid Solidification and Addition of Cu3P on the Mechanical Properties of Hypereutectic Al-Si Alloys
MATERIALS RESEARCH-IBERO-AMERICAN JOURNAL OF MATERIALS(2016)
摘要
The combined processes; rapid solidification, addition of Cu3P compound and heat treatments to improve the mechanical properties of the hypereutectic Al-13Si, Al-20Si and Al-20Si-1.5Fe-0.7Mn alloys (in wt. %) was studied. Optical microscopy and scanning electron microscopy were used to characterize the microstructures. The mechanical properties were evaluated by tensile tests. It was found that the cooling rate (20-50 degrees C/s) used to solidify the alloys plus the addition of Cu3P compound favored the formation of fine primary Si and the transformation of the Al/Si eutectic from acicular to semi-transformed morphology. The spheroidization of the Al/Si eutectic after heat treatment caused an increase in the elongation (%) compared with the as-cast alloys. Al-13Si alloy showed the highest UTS and elongation (%) values, reaching values up to 215 MPa and 9.6%, respectively. On the other hand, the Al-20Si-1.5Fe-0.7Mn alloy showed the lowest UTS (180MPa) and elongation (3.4%) values. The formation of the Fe-intermetallic compounds caused a negative effect on the mechanical properties of the Al-20Si-1.5Fe-0.7Mn alloy.
更多查看译文
关键词
Aluminum alloys,Semi-rapid solidification,Heat treatment,Microstructure,Mechanical properties
AI 理解论文
溯源树
样例
![](https://originalfileserver.aminer.cn/sys/aminer/pubs/mrt_preview.jpeg)
生成溯源树,研究论文发展脉络
Chat Paper
正在生成论文摘要