Effect Of Elements On Hot Tearing Of Directionally Solidified Ni-Based Superalloys
ADVANCES IN COMPOSITES, PTS 1 AND 2(2011)
摘要
The effect of elements such as Ti, Al, Hf, Zr and B on hot tearing susceptibility during directional solidification was explored by tube-like samples with thickness of 1.0 mm, 1.5mm and 2.0mm in wall. Results of SEM of elements on solidification of casting Ni-based superalloys were presented. The influential extent among the investigated elements is found to be: the largest is Ti, then Zr, B and Al, and Hf is the smallest. Titanium promotes the formation of (gamma+gamma') eutectic, increases sizes of the eutectic. Increasing Al content results in the size of gamma+gamma' eutectic and the number of gamma'. Increasing Zr content promotes gamma+gamma' eutectic.Varying B content shows little microstructural evolution.
更多查看译文
关键词
hot tearing,Ni-based superalloys,Directional solidification,Microstructure
AI 理解论文
溯源树
样例
![](https://originalfileserver.aminer.cn/sys/aminer/pubs/mrt_preview.jpeg)
生成溯源树,研究论文发展脉络
Chat Paper
正在生成论文摘要