Structure And Magnetic-Properties Of Mnbidy(Sm) Permanent Magnetic-Films
JOURNAL OF APPLIED PHYSICS(1995)
摘要
We have studied crystal texturing and magnetic properties of MnBiDy(Sm) permanent magnetic films, with thicknesses varying from 60 to 1200 nm, fabricated by the thermal coevaporation method and subsequently annealed in a vacuum oven at temperatures ranging from 350-425��C. X-ray diffraction analysis has shown that the samples exhibit low-temperature phase MnBi with a NiAs-type structure when the thicknesses of the samples are less than 250 nm. When the thicknesses are larger than 250 nm, however, the Bi3Mn 2 phase also appears. Magnetic measurements have revealed that saturation magnetization ��s=46-78 emu/g, residual magnetic induction Br=3.2-7.3 kGs, remnant magnetization ratio r=0.64-0.98, intrinsic coercive force Hc=2.2-7.3 kOe, and magnetic energy product (BH)m=3.33-14.3 MGOe. We have also found that Hc depends on the thickness of the sample, and reaches a maximum when the thickness d=400 nm. The origin of the coercive force may be understood by the nucleation and growth of reverse magnetic domains when d<150 nm but by domain rotation when d?600 nm. ? 1995 American Institute of Physics.
更多查看译文
关键词
magnetic properties,magnetic domains,permanent magnet,microstructures,energy production,x ray diffraction
AI 理解论文
溯源树
样例
![](https://originalfileserver.aminer.cn/sys/aminer/pubs/mrt_preview.jpeg)
生成溯源树,研究论文发展脉络
Chat Paper
正在生成论文摘要