Magnetic switching driven by spin-orbit torque in topological-insulator-based (Bi_0.5Sb_0.5)₂Te₃/Ta/CoFe/Cu/ CoFe/IrMn heterostructure

The giant spin-orbit torque (SOT) generated by topological surface states in topological insulators (TIs) provides an energy-efficient writing method for magnetic memory. In this study, we demonstrate a topological insulator/spin valve (TI/SV) device that operates at room temperature. An ultrathin, high-quality TI (Bi0.5Sb0.5)(2)Te-3 (BST) thin film is epitaxially grown as a functional layer on a (0001)-Al2O3 substrate via molecular beam epitaxy in ultrahigh vacuum. Subsequently, Ta/CoFe/Cu/CoFe/IrMn layers are grown on BST/Al2O3 thin films using magnetron sputtering to form TI/SV devices via a subsequent standard lithography process. The resulting TI/SV devices exhibit a giant magnetoresistance of up to similar to 1.1% at room temperature. Additionally, a low switching current density of approximately 1.25 x 10(5) A cm(-2) is achieved, which implies high potential for further reducing the energy consumption of SOT-based devices. The SOT conversion efficiency and charge-spin conversion efficiency of the TI layer are approximately 4.74 x 10(-6) Oe A(-1) cm(2) and 1.33, respectively, as extracted from the SOT-induced shift of the magnetic switching field. Moreover, the switching current density reduces steadily with the device size scaling down. This study can facilitate the realization of energy-efficient magnetic memory devices in the future.