Efficient separation of impurities Fe/Al/Ca and recovery of Zn from electroplating sludge using glucose as reductant.

Electroplating sludge (ES), a hazardous waste containing heavy metals and Fe/Al/Ca impurities, is conventionally disposed of in landfills. In this study, a pilot-scale vessel with an effective capacity of 20 L was applied to recycle Zn from real ES. The sludge contained 6.3 wt% Fe, 6.9 wt% Al, 2.6 wt% Si, 6.1 wt% Ca, and 17.6 wt% Zn and was treated using a four-step method. First, ES was dissolved in nitric acid after washing in a water bath at 75 °C for 3 h to produce an acidic solution with Fe, Al, Ca, and Zn concentrations of 4527.2, 3116.1, 3357.7, and 21,275 mg/L, respectively. Second, the acidic solution was added with glucose at an Mglucose/Mnitrate ratio of 0.08 and hydrothermally treated at 160 °C for 4 h. During this step, nearly 100 % Fe and 100 % Al were simultaneously removed as a mixture containing 53.1 wt% Fe2O3 and 45.7 wt% AlO. This process was repeated five times, during which the Fe/Al removal and Ca/Zn loss rates remained unchanged. Third, the residual solution was adjusted with sulfuric acid, and over 99 % Ca was removed as gypsum. The residual Fe, Al, Ca, and Zn concentrations were 0.44, 0.88, 52.59, and 31,177.1 mg/L, respectively. Finally, Zn in the solution was precipitated as ZnO with a concentration of 94.3 %. Economic calculations showed that each 1 t of ES processed created revenue of about $122. This is the first study of high-value metal resource recovery using real electroplating sludge at the pilot scale. This work highlights the pilot-scale application of resource utilization of real ES and provides new insights into the recycling of heavy metals from hazardous waste.