Tribological Behavior of Ti-Coated Diamond/Copper Composite Coating Fabricated via Supersonic Laser Deposition

Diamond/copper composite coating is promising for wear-resistant applications, owing to the extreme hardness of the diamond reinforcement. Ti-coated diamond/copper composite coatings with various laser powers were successfully fabricated employing the novel manufacturing technology of supersonic laser deposition (SLD). Ti-coated diamond, which was able to enhance the wettability between diamond and copper, was prepared at the optimal parameters via salt bath. Nano-spherical titanium carbides were uniformly distributed on the diamond's surface to generate a favorable interface bonding with a copper matrix though mechanical interlocking and metallurgical bonding during impact. Furthermore, the results showed that the transition layer acted as a buffer, preventing the breakage of the diamond in the coating. SLD can prevent the graphitization of the diamonds in the coating due to its low processing temperature. The coordination of laser and diamond metallization significantly improved the tribological properties of the diamond/copper composite coatings with the SLD technique. The microhardness of the diamond/copper composite coating at a laser power of 1000 W reached about 172.58 HV0.1, which was clearly harder than that of the cold sprayed copper. The wear test illustrated that the diamond/copper composite coating at a laser power of 1000 W exhibited a low friction coefficient of 0.44 and a minimal wear rate of 11.85 mu m(3) center dot N-1 center dot mm(-1). SLD technology shows great potential in the field of preparing wear-resistant hard reinforced phase composite coatings.