Carbon-Coated Si Nanoparticles Anchored on Three-Dimensional Carbon Nanotube Matrix for High-Energy Stable Lithium-Ion Batteries

An easy and scalable synthetic route was proposed for synthesis of a high-energy stable anode material composed of carbon-coated Si nanoparticles (NPs, 80 nm) confined in a three-dimensional (3D) network-structured conductive carbon nanotube (CNT) matrix (Si/CNT@C). The Si/CNT@C composite was fabricated via in situ polymerization of resorcinol formaldehyde (RF) resin in the co-existence of Si NPs and CNTs, followed by carbonization at 700 degrees C. The RF resin-derived carbon shell (similar to 10 nm) was wrapped on the Si NPs and CNTs surface, welding the Si NPs to the sidewall of the interconnected CNTs matrix to avoid Si NP agglomeration. The unique 3D architecture provides a highway for Li+ ion diffusion and electron transportation to allow the fast lithiation/delithiation of the Si NPs; buffers the volume fluctuation of Si NPs; and stabilizes solid-electrolyte interphase film. As expected, the obtained Si/CNT@C hybrid exhibited excellent lithium storage performances. An initial discharge capacity of 1925 mAh g(-1) was achieved at 0.1 A g(-1) and retained as 1106 mAh g(-1) after 200 cycles at 0.1 A g(-1). The reversible capacity was retained at 827 mAh g(-1) when the current density was increased to 1 A g(-1). The Si/CNT@C possessed a high Si content of 62.8 wt%, facilitating its commercial application. Accordingly, this work provides a promising exploration of Si-based anode materials for high-energy stable lithium-ion batteries.