Disordered interfaces of alkaline aluminate salt hydrates provide glimpses of Al 3+ coordination changes.

In contrast to classical dissolution, aluminum coordination change proceeds through a dynamically stabilized ensemble of intermediate states in a disordered layer at the solid-solution interface. In both melting and dissolution of NSA, octahedral, monomeric aluminum transition through an intermediate of pentahedral coordination. The intermediate dehydroxylates to form tetrahedral aluminate (Al(OH)) in the liquid phase. This coordination change is concomitant with a breaking of the ionic aluminate-sodium ionlinkages. The solution phase Al(OH) ions subsequently polymerize into polynuclear aluminate ions. However, there are some differences between bulk melting and interfacial dissolution, with the onset of the surface-controlled process occurring at a lower temperature (∼30 °C) and the coordination change taking place more gradually as a function of temperature. This work to determine the local structure and dynamics of aluminum in the disordered layer provides a new basis to understand mechanisms controlling aluminum phase transformations in highly alkaline solutions.