Piezoelectric properties of (Na, K)(Nb, Sb)O-3-CaZrO3 thin film grown on Sr2Nb3O10 perovskite oxide nanosheet at low temperatures

A Sr2Nb3O10 (SNO) nanosheet was deposited on a Pt/Ti/SiO2/Si (Pt-Si) substrate using the Langmuir-Blodgett technique. An SNO monolayer was used as the seed layer for the growth of a crystalline 0.97(Na0.5K0.5)(Nb0.91Sb0.09)O-3-0.03CaZrO(3) (NKNS-CZ) thin film at a low temperature of 400 degrees C. The NKNS-CZ thin film grew along the [001] direction, and it had a dense microstructure with an average grain size of 75 nm. The dielectric constant of the film was 250, with a low dielectric loss of 3.5% at 100 kHz. The leakage current density of the Pt/NKNS-CZ top-electrode interface was approximately 1.3 x 10(-6) A/cm(2) at 0.05 MV/cm. Additionally, a slightly increased leakage density (8.1 x 10(-6) A/cm(2) at 0.05 MV/cm) was observed at the NKNS CZ/SNO/Pt Si bottom-electrode interface. Hence, the film exhibited relatively good insulating properties. The d(33) and d(33) x g(33) values of the thin film were approximately 270 pm/V and 32.9 pm(2)/N, respectively. These are the largest d(33) and d(33) x g(33) values reported until now. Therefore, the NKNS CZ thin film shows excellent piezoelectric properties, and it can be used for fabricating thin-film piezoelectric energy harvesters. Published under an exclusive license by AIP Publishing.