Microstructure, Mechanical and Tribological Properties of Ta(C,N) Coatings Deposited on Ta15 Substrates with Different Nitrogen Partial Pressure
Social Science Research Network(2022)
摘要
PurposeThe purpose of this paper is to obtain the optimal N-2/Ar ratio parameters for preparing Ta (C, N) coating. Three coatings with different N-2/Ar ratios were prepared on the TA15 substrate, and their effects on the wear properties of the coatings were discussed. Design/methodology/approachTa(C, N) coatings with three different N-2/Ar ratios were prepared on TA15 substrates using the double cathode glow metallurgical plasma alloying technique (DGMPA) using a step-by-step diffusion method. FindingsWith the increase of N-2/Ar flow ratio, the hardness and elastic modulus of the coating first increase and then decrease. Compared with the S1 sample (N-2/Ar gas ratio 25: 75) and the S3 sample (N-2/Ar gas ratio 75: 25), the S2 sample (N-2/Ar gas ratio 50: 50) has better mechanical properties, with hardness increased by 48.45% and 6.8%, respectively, and elastic strain ratio increased by 22.8% and 28.5%, respectively. Moreover, the wear degree of the S2 sample is less than other samples. The wear rate of the S2 sample was 32.4% lower than the S3 sample at 300 degrees C and 14.3% lower than the S3 sample at 500 degrees C. Therefore, the S2 sample has the best mechanical properties and the best high temperature wear resistance. Originality/valueTa(C, N) coatings were prepared by DGMPA technology, and the wear mechanism of Ta(C, N) coatings with different N-2/Ar ratios was investigated to reduce the wear rate.
更多查看译文
关键词
DGMPA,Ta(C,N) coating,N-2,Ar flow ratio,Tribological properties
AI 理解论文
溯源树
样例
生成溯源树,研究论文发展脉络
Chat Paper
正在生成论文摘要