Facile and template-free synthesis of nano-macroporous LaCoO 3 perovskite oxide for efficient diesel soot oxidation

The basic LaCoO 3 perovskite oxides were prepared by the series of methods (reverse co-precipitation, citric acid aided sol–gel, glycine assisted solution combustion), underwent physicochemical characterization (XRD, FTIR, BET, XPS and SEM), followed by their soot oxidation activity tests in both “loose” and “tight” conditions of soot-catalyst contact. The activity tests revealed that the LaCoO 3 catalyst formed using glycine assisted combustion synthesis gives the best performance with the T 10 , T 50 , and T 90 at 361 °C, 404 °C and 445 °C, respectively, in loose contact conditions and T 10 , T 50 , and T 90 at 306 °C, 330 °C and 355 °C, respectively, in tight contact conditions. Its outstanding performance can be attributed to its unique morphology consisting of scaffolds having an extensively interconnected macroporous network with macropores having nanoporous struts as walls as evidenced by SEM results. Such morphology makes the active sites of inner pores accessible to the gaseous (air) as well solid reactant (soot particles), thereby benefitting soot oxidation reaction.