Mechanochemically Synthesized Zif-8 Nanoparticles Blended Into 6fda-Trmpd Membranes For C3h6/C3h8 Separation

The mixed matrix membranes (MMMs) consisting zeolitic-imidazolate framework-8 (ZIF-8) nanoparticles in a polymer have been of considerable interest in separation applications. The fillers used are mostly synthesized using the solvothermal method. In this study, the ZIF-8 nanoparticles were synthesized using a solvent-less and salt-free mechanochemical method and were added to 6FDA-TrMPD polyimide to prepare MMMs. The single gas permeation of C3H6 and C3H8 through the MMMs was investigated. The C3H6 permeability and C3H6/C3H8 ideal selectivity of a 20 wt% mechano-synthesized ZIF-8/6FDA-TrMPD MMM were 70% and 32% higher than those of the neat polymer membrane at 0.1 MPa and 308 K, respectively. The C3H6/C3H8 separation performance of the mechano-synthesized ZIF-8 MMM was similar to that of the conventional solvothermal-synthesized ZIF-8 MMM. This separation performance was in good agreement with the Maxwell model. Temperature and pressure dependence analyses confirmed that the mechano-synthesized ZIF-8 nanoparticles acted as molecular sieves in the MMMs for the C3H6 and C3H8 permeation.