A Low-Temperature Preparation Strategy Of Sic/Zrb2-Crsi2-Si/Sic Multilayer Oxidation-Resistant Coating For C/C Composites: Process, Kinetics And Mechanism Research

In this work, a strategy of preparing multilayer SiC/ZrB2-CrSi2-Si/SiC coating at low-temperature by combining chemical vapor deposition (CVD), brush-sintering and preoxidation was proposed for C/C composites. The coated C/C composites could maintain stable and long-term oxidation resistance at 1473-1673 K, and the specific mass loss was only 8.05 mg center dot cm-2 after 1673 K/340 h oxidation. The coupling mechanism of the preparation process on the microstructure and performance, the kinetics process of oxidation behavior and the protection/failure mechanism of the coating were analyzed. Furthermore, the importance of organosilicon (SiCxOy) in the process of self-healing and oxidation resistance was enlightened.