Effect of hot rolling reduction and annealing treatment on grain boundary character distribution in austenitic low-density Fe-Mn-Al-C-Cr steel

•Grain boundary engineering was performed by simple annealing treatment.•Large reduction of hot rolling promoted the formation of CSL boundaries.•The connectivity of random high angle grain boundaries was broken.•The grain cluster formed by multiple-twinning after annealing was observed.