Experimental Study on Improvement Mechanism of Silane Emulsion on Acid Rain Corrosion of Green Ecological Concrete

Concrete structure is vulnerable to acid rain corrosion, which affects the service life of the material, in the corrosive environment, and concrete structure will deteriorate because of the erosion of water/chloride ions. Therefore, waterproof treatment of concrete structure is needed to improve the durability of the structure. In this study, the green ecological concrete is taken as the research object. The concrete is mixed with a certain amount of silane emulsion to reduce the probability of corrosion of concrete due to moisture and chloride ions, thereby prolonging the service life of this kind of concrete. During the experiment, in order to further test the corrosion resistance of silane emulsion to this kind of concrete, different kinds of concrete were taken as test objects and divided into 3 test groups, namely, the original test group (ITE), the non silane emulsion test group (TWSE) and the optimal ratio test group (OT-SE). It is proved by experiments that the best proportion of concrete mixed with silane emulsion is 0.32 of water binder ratio, 18% of coal powder mixing ratio, 37% of gravel mixing ratio and 0.23% of proportion of silane emulsion. The above factors are applied to compressive strength test, and 30 days as test time, the compressive strength of concrete with fly ash is measured. In the experiment of anticorrosion, compared with the traditional concrete samples, the electrical flux of concrete mixed with silane emulsion decreased by 28.7% in 8 h, that is, chloride ion permeability decreased significantly.