The formation of discontinuous gradient regimes during crack initiation in high strength steels under very high cycle fatigue

•Discontinuous gradient regimes are observed during crack initiation in VHCF regime.•The gradient ultrafine grains result from excessive cyclic plastic deformation.•The equivalent crack growth rate in FGA is in the magnitude of 10−12–10−11 m/cyc.